In this paper, the effect of changes the parameters of heat treatment on the structure and the degree of elements segregation was determined, in the context of corrosion resistance of ductile iron Ni-Mn-Cu, containing 7.2% Ni, 2.6% Mn and 2.4% Cu. In the condition after casting, castings of austenitic matrix and 160HBW hardness were obtained. The achieved castings were soaked at 450, 550 and 650°C for 4, 8 and 12 hours, then cooled down at the ambient air. In most cases, the heat treatment resulted in a change in the castings matrix, had the consequence of increasing their hardness in comparison to raw castings. Increasing the temperature and prolonging soaking time resulted in increasing the degree of transformation of austenite, while reducing the degree of elements segregation. This led to the formation of slightly bigger number of pitting due to corrosion, but not so deep and more evenly distributed in comparison to raw castings. Wherein the results of corrosion tests show that heat treatment of castings did not significantly change their corrosion resistance in comparison to raw castings, in contrast to the significant increase in mechanical properties.
The object of the experimental studies was to determine the mechanical properties of a hypoeutectic EN AC - 42100 (EN ACAlSi7Mg0,3) silumin alloy, where the said properties are changing as a result of subjecting the samples of different types to solution treatment. An important aspect of the studies was the use type of device for the heat treatment. As a basic parameter representing the mechanical properties, the tensile strength of the metal (Rm) was adopted.
The paper presents the results of examination concerning optimization of the σ phase precipitates with respect to the functional properties of ferritic-austenitic cast steel. The examined material comprised two grades of corrosion-resistant cast steel, namely GX2CrNiMoN25-6-3 and GX2CrNiMoCuN25-6-3-3, used for example in elements of systems of wet flue gas desulphurisation in power industry. The operating conditions in media heated up to 70°C and containing Cl- and SO4 ions and solid particles produce high erosive and corrosive wear. The work proposes an application of the σ phase as a component of precipitation strengthening mechanism in order to increase the functional properties of the material. Morphology and quantities of σ phase precipitates were determined, as well as its influence on the erosion and corrosion wear resistance. It was shown that annealing at 800°C or 900°C significantly improves tribological properties as compared with the supersaturated state, and the best erosion and corrosion wear resistance achieved due to the ferrite decomposition δ → γ’ + σ was exhibited in the case of annealing at the temperature of 800°C for 3 hours.
The study presents the results of research aimed at the construction of a model of the relationship between the physical properties of metal and the types of toughening treatment and modifiers used in the modification of BA1044 alloy. Samples of melts were subjected to four variants of the heat treatment and to five types of modification. Studies of the samples consisted in measurements of five physical parameters. Consequently, it was necessary to seek a relationship between the nine input parameters and five output parameters. With this number of the variables and a limited number of samples, searching for the relationships by way of statistical methods was obviously impossible, so it was decided to create an approximate model through the use of fuzzy logic. This study describes the process of creating a model and presents the results of some simulation experiments that confirm the validity of the correct approach.
The lifetime of guide grates in pusher furnaces for heat treatment could be increased by raising the flexibility of their structure through, for example, the replacement of straight ribs, parallel to the direction of grate movement, with more flexible segments. The deformability of grates with flexible segments arranged in two orientations, i.e. crosswise (perpendicular to the direction of compression) and lengthwise (parallel to the direction of compression), was examined. The compression process was simulated using SolidWorks Simulation program. Relevant regression equations were also derived describing the dependence of force inducing the grate deformation by 0.25 mm ‒ modulus of grate elasticity ‒ on the number of flexible segments in established orientations. These calculations were made in Statistica and Scilab programs. It has been demonstrated that, with the same number of segments, the crosswise orientation of flexible segments increases the grate structure flexibility in a more efficient way than the lengthwise orientation. It has also been proved that a crucial effect on the grate flexibility has only the quantity and orientation of segments (crosswise / lengthwise), while the exact position of segments changes the grate flexibility by less than 1%.
A research of wear resistance of an austenitic cast iron with higher resistance to abrasive-wear and maintained corrosion resistance characteristic for Ni-Resist cast iron is presented. For the examination, structure of raw castings was first formed by proper selection of chemical composition (to make machining possible). Next, a heat treatment was applied (annealing at 550 °C for 4 hours followed by air cooling) in order to increase abrasive-wear resistance. One of the factors deciding intensity of wear appeared to be the chilling degree of castings. However, with respect to unfavourable influence of chilling on machining properties, an important factor increasing abrasivewear resistance is transformation of austenite to acicular ferrite as a result of annealing non-chilled castings. Heat treatment of non-chilled austenitic cast iron (EquNi > 16%) resulted in much higher abrasive-wear resistance in comparison to the alloy having pearlitic matrix at ambient temperature (EquNi 5.4÷6.8%).
The author has developed and patented several types of gas cupola furnaces, which, due to replacing coke with gas, do not emit carbon monoxide, sulfur dioxide and coke dust. The author has defined the optimal modes of gas-and-air mixture combustion, i.e. the optimal coefficient of air discharge and gas mixture escape speed in melting cast iron. It has been experimentally proved that from the point of view of obtaining the maximum temperature, the optimal was the process with some lack of air, i.e. with α = 0.98. The results of metallurgical studies used in the article allowed to develop an optimal structure of the gas cupola furnace with a heterogeneous refractory filling, and to establish the optimal composition of the filling. For the first time the optimal composition of the filling is given: 40% of chamotte, 30% of high-alumina refractory, 30% of electrode scrap. It has been noted that when gas cupola furnaces were used, the main environmental advantage was the reduction of dust emission into the atmosphere, CO and SO2 content.
The article describes the problem of selection of heat treatment parameters to obtain the required mechanical properties in heat- treated bronzes. A methodology for the construction of a classification model based on rough set theory is presented. A model of this type allows the construction of inference rules also in the case when our knowledge of the existing phenomena is incomplete, and this is situation commonly encountered when new materials enter the market. In the case of new test materials, such as the grade of bronze described in this article, we still lack full knowledge and the choice of heat treatment parameters is based on a fragmentary knowledge resulting from experimental studies. The measurement results can be useful in building of a model, this model, however, cannot be deterministic, but can only approximate the stochastic nature of phenomena. The use of rough set theory allows for efficient inference also in areas that are not yet fully explored.
This scientific paper presents the research on influence of austenitizing temperature on kinetics and evolution of the spheroidal plain cast iron during eutectoid reaction in isothermal conditions. The cast iron has been austenitized in temperatures of 900, 960 or 1020°C. There were two temperature values of isothermal holding taken into consideration: 760 or 820°C. The order of creation of reaction products and their morphology have been analyzed. The particular attention has been paid to the initial stage of transformation. The qualitative research has been executed using the transmission electron microscope (TEM), as well as quantitative research (LM). The influence of austenitizing temperature has also been determined on transformation kinetics and structural composition. It was found that the increase of austenitizing temperature is conductive to the initial release of structures by metastable system. A reduction of time was observed of the initial stage of transformation at temperature close to Ar12 with its simultaneous elongation at temperature close to Ar11, with an increase of austenitizing temperature. The dependences obtained by the metallographic method confirm the prior results of dilatometric research of eutectoid reaction.
Creep-resistant parts of heat treatment furnaces are in most cases made from high-alloyed chromium-nickel and nickel-chromium iron alloys, both cast and wrought. This paper presents the types of casting alloys used for this particular purpose, since the majority of furnace components are made by the casting process. Standards were cited which give symbols of alloy grades used in technical specifications by the domestic industry. It has been indicated that castings made currently are based on a wider spectrum of the creep-resistant alloy grades than the number of alloys covered by the standards. Alloy grades recommended by the technical literature for individual parts of the furnace equipment were given. The recommendations reflect both the type of the technological process used and the technical tasks performed by individual parts of the furnace equipment. Comments were also made on the role of individual alloying elements in shaping the performance properties of castings.
The paper presents the effect of pre-heat treatment on the mechanical properties of ductile cast iron with elevated content of Cu and Mo elements. Austempered Ductile Iron is a material with non-standard properties, combining high tensile strength and abrasion resistance with very good plasticity. In addition, it is prone to strain hardening and have good machining abilities. The study was conducted for five designed heat treatment cycles. The variables were the time and temperature of the pre-heat treatment, followed by one of two standard heat treatments for ADI cast iron. The aim of the authors was fragmentation of the grains of perlite during the initial heat treatment. It is presumed, that subsequent heat treatment will cause further refinement of the microstructure than would be the case without initial heat treatment. Diffusion is much faster than in case of ferritic matrix of cast iron. The results will be used to evaluate material for the production of parts of equipment that must operate under extreme load conditions.
The main aim of this study was to examine the compression-induced state of stress arising in castings of the guide grates during operation in pusher-type furnaces for heat treatment. The effect of grate compression is caused by its forced movement in the furnace. The introduction of flexible segments to the grate structure changes in a significant way the stress distribution, mainly by decreasing its value, and consequently considerably extends the lifetime of the grates. The stress distribution was examined in the grates with flexible segments arranged crosswise (normal to the direction of the grate compression) and lengthwise (following the direction of force). A regression equation was derived to describe the relationship between the stress level in a row of ribs in the grate and the number of flexible segments of a lengthwise orientation placed in this row. It was found that, regardless of the distribution of the flexible segments in a row, the stress values were similar in all the ribs included in this row, and in a given row of the ribs/flexible segments a similar state of stress prevailed, irrespective of the position of this row in the whole structure of the grate and of the number of the ribs/flexible segments introduced therein. Parts of the grate responsible for the stress transfer were indicated and also parts which play the role of an element bonding the structure.
In the paper the results and analysis of corrosion tests were presented for low-alloyed cast steel in as-cast state and after heat treatment operations. Such alloys are applied for heavy loaded parts manufacturing, especially for mining industry. The corrosion test were performed in conditions of high salinity, similar to those occurring during the coal mining. The results have shown, that small changes in chemical composition and the heat treatment influence significantly the corrosion behaviour of studied low-alloyed cast steels.
Silicon – molybdenum cast iron commonly called SiMo due to its unique properties has becoming more and more interesting engineering material. The history and development of this alloy is relatively long but, due to the significant difficulties during the manufacturing process resulting in the lower final quality than expected, it has not been applied to often in practice. The biggest challenge is its brittleness as a result of the carbides precipitations. During last few years, thanks to the many important researches made and the general foundry technology development, the interest in SiMo iron has been rapidly growing, especially for the castings for heavy duty applications like corrosion, high temperature and wear abrasion resistant parts. In the article the heat treatment attempts to improve the microstructure of SiMo castings has been presented. The goal was to destroy or at least to refine and uniformly distribute the carbides precipitations to improve mechanical properties of the exhaust manifold castings for the cars. The experiments were carried out for the alloy contains approx. 4% Si, 1% Mo and 3.2%C. The range of the research included: hardness measuring, standard mechanical properties and microstructure for as-cast state and after that the subsequent heat treatment process with another properties check. The result of the heat treatment was the elimination of pearlite from the metal matrix. Moreover, the changes of the carbide molybdenum – rich phase morphology were observed. The dispersion of the carbides precipitations in the carbides area was observed. The experiments proved the possibility to control the microstructure and the mechanical properties of the SiMo castings by means of heat treatment but only to some extent.
The paper presents the possibility of the usage of the concfocal microscope for define the type of tribological wear present during the technical dry friction on the testing machine of the pin-on-disc T-01M. The pin was a remelted high-speed steel and the disc was made from sintered carbides. The surface layer of the high-speed steel was remelted with the electric arc with different parameters. The intensity of the electric arc current was changed, the scanning speed and the single, overlapping remeltings were used. On the basis of the 3D, 2D view of the surface friction of the pin (made from the remelted high-speed steel), disc (made from the sintered carbides) and the surface roughness profile run along the marked line, the presence of the abrasive wear can be defined with the description of the elementary wear processes due to the abrasive and/or adhesive wear.
By the very nature of their work, castings used in furnaces for heat treatment and thermo-chemical treatment are exposed to the effect of many unfavorable factors causing their deformation and cracking, significantly shortening the lifetime. The main source of damage are the micro- and macro-thermal stresses appearing in each cycle. As the cost of furnace instrumentation forms a significant part of the total furnace cost, in designing this type of tooling it is important to develop solutions that delay the damage formation process and thus extend the casting operation time. In this article, two structural modifications introduced to pallets castings to reduce thermal stresses arising at various stages of the cooling process are proposed. The essence of the first modification consists in making technological recesses in the wall connections, while the aim of the second one is to reduce the stiffness of the pallet by placing expanders in the external walls. Using the results of simulation analyses carried out by the finite element method, the impact of both proposed solutions on the level of thermal stresses was evaluated.
The aim of the current study was to examine the structure of an alloy treated at various temperatures up to 2,000–2,100 °C. Among research techniques for studying alloy structure there were the electron and optical microstructure, X-ray structure, and spectral analysis, and for studying the developed furnace geometric parameters the authors employed mathematical modeling method. The research was performed using aluminum smelting gas-fired furnaces and electric arc furnaces. The objects of the study were aluminum alloys of the brand AK7p and AK6, as well as hydrogen and aluminum oxide in the melt. For determining the hydrogen content in the aluminum alloy, the vacuum extraction method was selected. Authors have established that treatment of molten aluminum alloy in contact with carbon melt at high temperatures of 2,000–2,100 °C has resulted in facilitating reduction of hydrogen and aluminum oxide content in the melt by 40-43% and 50-58%, respectively, which is important because hydrogen and aluminum oxide adversely affect the structure and properties of the alloy. Such treatment contributes to the formation of the extremely fine-grained microstructure of aluminum alloy.
This article deals with the fatigue properties of newly used AlZn10Si8Mg aluminium alloy where the main aim was to determine the fatigue strength and compare it with the fatigue strength of AlSi7Mg0.3 secondary aluminium alloys which is used in the automotive industry for cyclically loaded components. AlZn10Si8Mg aluminium alloy, also called UNIFONT 90, is self-hardening (without heat treatments), which contributes to economic efficiency. This is one of the main reasons why is compared, and may be an alternative replacement for AlSi7Mg0.3 alloy which is heat treated to achieve required mechanical properties. The experiment results show that the fatigue properties of AlZn10Si8Mg alloy are comparable, if not better, than AlSi7Mg0.3 alloy. Fatigue properties of AlZn10Si8Mg alloy are achieved after seven days of natural ageing, immediately after casting and achieving value of fatigue strength is caused by structural components formed during solidification of the melt.
The article describes the trend towards increased use of induction crucible furnaces for cast iron smelting. The use of gas cupola’s duplex process – induction crucible furnace – has been proved the effective direction of scientific and technical advance in the foundry industry. Gas cupolas and induction furnaces are used for cast iron smelting at the Penza Compressor Plant where in the 1960s the author developed and introduced gas cupolas for the first time in the world. In the article, the author represents the findings of the investigation on thermodynamics of crucible reduction of silicon, which is pivotal when choosing the technological mode for cast iron smelting in induction furnaces. The author proposes a new reaction crucible diagram with due account of both partial pressure and activity of the components involved into the process. For the first time ever, the electrochemical mechanism of a crucible reaction has been studied and the correctness of the proposed diagram has been confirmed.
This paper deals with influence of chrome addition and heat treatment on segregation of iron based phases in the secondary alloy AlSi7Mg0.3 microstructure by chrome and heat treatment. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich intermetallic phases. It is impossible to remove iron from melt by standard operations, but it is possible to eliminate its negative influence by addition some other elements that affect the segregation of intermetallics in less harmful type or by heat treatment. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of chrome as iron corrector of iron based phases.
In the course of homogenizing annealing of aluminium alloys being cast continually or semi-continually it appears that chemical inhomogenity takes off within separate dendritic cells (crystal segregation). It is about a diffusion process that takes place at the temperature which approaches the liquid temperature of the material. In that process the transition of soluble intermetallic compounds and eutectic to solid solution occurs and it suppresses crystal segregation significantly . The temperature, homogenization time, the size of dendritic cells and diffusion length influences homogenizing process. The article explores the optimization of homogenizing process in terms of its time and homogenizing annealing temperature which influence mechanical properties of AlZn5,5Mg2,5Cu1,5 alloy.
The aim of that work was the evaluation of the quality of welded connections elements (welds) from the 30HGS steel and titanium alloy Ti6Al4V. The metallographic, factographic tests were used, and measurements of microhardness with the Vickers method. In the head weld of the 30HGS steel there were non-metallic partial division and bubbles observed. The average microhardness in the head connection was 320 HV0.1. There was no significant increase/decrease observed of microhardness in the head influence zone of the weld. There was a good condition of head connections observed, in accordance with the standard EN12517 and EN25817. In the head weld of Ti6Al4V titanium alloy there were single, occasional non-metallic interjections and bubbles observed. There were no cracks both on the weld, and on the border of the heat influence zone. The value of microhardness in head connection was in the range 300÷445 HV0.1. Reveal a very good condition of the head connections in accordance with the standard EN12517 and EN25817. The factographic tests prove the correctness of welded connections done and then heat treatment in case of steel and titanium alloy.