The paper presents the capabilities of welding techniques to creating properties of wear resistant high chromium cast iron alloy. The use of the right kind of welding sequence allows you to change the structure and properties of the obtained welds. Tests were conducted for one type of additive material in the form of self shielded core wire. In order to determine the effect of the type of welding sequence on the properties of welds performed welding using string bead and weave bead. The resulting weld was tested on hardness and research structure in an optical microscope. In the following studies have been made erosive tests wear of made hardfacing. String beads gave structure rich in carbides and harder about 270 HV of the weld with weave bead. Also, wear resistance was nearly twice as better for welds made with string beads. In the experiment a decisive role in the resistance to wear plays a high hardness of the deposit and the presence of carbides in its structure. Changes in the basic parameters of the deposition process allows for the formation of structure and properties of hardfacing welds in a wide range.
The paper deals with susceptibility of nodular cast iron with ferritic -pearlitic matrix on cavitation erosion . Cavitation tests were carried out with the use of a cavitation erosion vibratory apparatus employing a vibration exciter operated at frequency of 20 kHz. The study allowed to determine the sequence of subsequent stages in which microstr ucture of cast iron in superficial regions is subject to degradation. The first features to be damaged are graphite precipitates. The ferritic matrix of the alloy turned out to be definitely less resistant to cavitation erosion compared to the pearlitic matrix component.
This paper presents a numerical analysis of an agitated fully baffled cylindrical vessel with a down pumping four blade worn or unworn pitched blade impeller (α = 45° and 30°) under a turbulent flow regime. CFD simulations predict the pumping capacity of the system equipped by worn and unworn pitched blade impeller. Experimental data were taken from the authors’ previous work and compared with results of numerical computations. A good agreement with experimental data was obtained. The ensemble-average mean velocity field with worn and unworn impellers was computed. It follows from the simulation results that the wear rate of the impeller blade has a significantly negative effect on the velocity distribution in an agitated liquid. The greater the destruction of the worn blade, the higher is the deformation of the velocity field around the rotating impeller, with a simultaneous decrease in impeller pumping capacity.
Materials based on cast irons are often used for protection against wear. One of the methods of creating protective surface with cast iron structures is hardfacing. The application of hardfacing with self shielded flux cored wire with high carbon content is one of the economical ways often used to protect machinery parts exposed to both abrasion and erosion. The wear resistance of hardfacings depends on their chemical composition, structure obtained after hardfacing, parameters of depositing process and specific conditions of wear. As the base material in the investigation the steel grade S235JR was used. The wear behavior mechanism of hardfacings made with one type of self shielded flux cored wire and different process parameters were evaluated in this paper. Structures obtained in deposition process were different in hardness, amount of carbides and resistance to wear with two investigated impingement angles. The erosion tests showed that impingement angle 30° gives lower erosion rate than angle 60°.