Alkali-aggregate reactivity (AAR) is one of the major causes of damage in concrete. Potential susceptibility of aggregates to this reaction can be determined using several methods. This study compares gravel alkali reactivity results obtained from different tests conducted on coarse aggregates with complex petrography. The potential for the reactivity in the aggregates was revealed in the chemical test using treatment with sodium hydroxide. Optical microscopy, scanning electron microscopy and X-ray diffraction were used to identify the reactive constituents. The expansion measured in the mortar bars test confirmed that the aggregate was potentially capable of alkali silica reactivity with consequent deleterious effect on concrete.
Substituting of ethyl silicate with ecologic sols of colloidal silica in the investment casting technology, resulting from the increased demands concerning environmental protection, caused the prolongation of production cycle for precision castings produced in multi-layer thin-walled ceramic shell moulds. Modification of Sizol 030 binder with benzoyl peroxide, proposed in the paper, was aimed at restriction of time needed for realization of a single layer of the shell mould, and by the same, of such a mould as a whole. Examination of kinetics of the drying process were held for the layers made of prepared moulding material and the influence of binder modification on the mould curing time was determined.
Describes how to obtain a soluble sodium silicate with a density of 1.40 g/cm3, 1.45 g/cm3, 1.50 g/cm3, and silica module M = 2.1 obtained from the silica- sodium glass with module M = 3.3 and M = 2.1. Residual (final) strength of molding samples made with these binders, were determined at temperatures corresponding to the characteristic temperatures of phase and temperature transitions of silica gel. Indicated the type of soluble sodium silicate capable of obtain the smallest value of the final strength of molding sand in the specified range of temperatures.
The granary weevil, Sitophilus granarius (L.), is one of the most important internal feeders of stored grain. Nanotechnology has become one of the most promising new approaches for pest control in recent years. In our screening program, laboratory trials were conducted to determine the effectiveness of silica nanoparticles (SNPs) and zinc nanoparticles (ZNPs) against the larval stage and adults of S. granarius on stored wheat. Nanoparticles of silica and zinc were synthesized through a solvothermal method. They were then used to prepare insecticidal solutions of different concentrations and tested on S. granarius. Silica nanoparticles (SNPs) were found to be highly effective against S. granarius causing 100% mortality after 2 weeks. ZNPs were moderately effective against this pest.
Silica multichannel monoliths modified with zirconia, titania and alumina have been used as reactive cores of microreactors and studied in chemoselective reduction (MPV) of cyclohexanon/benzaldehyde with 2-butanol as a hydrogen donor. The attachment of metal oxides to the silica surface was confirmed by FT–IR spectroscopy, and dispersion of metal oxides was studied by UV–Vis spectroscopy. the catalytic activity of the lewis acid centres in both chemical processes decreased in the order zirconia > alumina > titania. This activity is in good agreement with dispersion and coordination of metal species. good stability of zirconia-grafted reactors was confirmed. high porosity of the monoliths and the presence of large meandering flow-through channels with a diameter of ca. 30 mm facilitate fluid transport and very effective mixing in the microreactors. The whole synthesis process is perfectly in line with trends of modern flow chemistry
The paper analyses the influence of chemical composition of silicone-based composites on their properties in the aspect of using them as long-term soft denture lining materials. Different concentrations of filler and methylhydrosiloxane-dimethylsiloxane copolymer were used. The filler was introduced into the composite with mechanical mixing combined with ultrasonic homogenization. Scanning electron microscopy was used to investigate the quality of filler dispersion. Shore A hardness, tensile strength, sorption, solubility and tensile bond strength to poly(methyl methacrylate) were measured. Tests show satisfactory results for some experimental composites, which met all the requirements for such materials.
The effect of additives on the densification behavior and mechanical properties of pure and additive (Zr, B and Mg)-added silica ceramics were investigated for their application to the matrix phase of a silica fiber reinforced silica (SiO2/SiO2f) composite. The additives affected the rate of densification and crystallization (or transformation) of the amorphous silica. Among the compositions, pure silica ceramics sintered at 900°C for 1 h showed the maximum flexural strength. Based on the results, SiO2/SiO2f was fabricated by a repeated vacuum-assisted infiltration method followed by the heat treatment at 900°C for 1 h. The relative density of the composite was 78.2% with a flexural strength of 22.4 MPa. Fractography revealed that the composite was damaged by strong bonding at the fiber/matrix interface and the fracture of fiber.
In this study, agar-based nanocomposite films containing ultra-porous silica aerogel particles were fabricated by gel casting using an aqueous agar/silica aerogel slurry. The silica aerogel particles did not show significant agglomeration and were homogeneously distributed in the agar matrix. Transmission electron microscopy observations demonstrated that the silica aerogel particles had a mesoporous microstructure and their pores were not incorporated into the agar polymer molecules. The thermal conductivities of the agar and agar/5 wt.% silica aerogel nanocomposite films were 0.36 and 0.20 W·m–1·K–1, respectively. The transmittance of the agar films did not decrease upon the addition of silica aerogel particles into them. This can be attributed to the anti-reflection effect of silica aerogel particles.
The effects of silica additive (Poraver) on selected properties of BioCo3 binder in form of an aqueous poly(sodium acrylate) and dextrin (PAANa/D) binder were determined. Based on the results of the thermoanalytical studies (TG-DTG, FTIR, Py-GC/MS), it was found that the silica additive results in the increase of the thermostability of the BioCo3 binder and its contribution does not affect the increase in the level of emissions of organic destruction products. Compounds from group of aromatic hydrocarbons are only generated in the third set temperature range (420-838°C). The addition of silicate into the moulding sand with BioCo3 causes also the formation of a hydrogen bonds network with its share in the microwave radiation field and they are mainly responsible for maintaining the cross-linked structures in the mineral matrix system. As a consequence, the microwave curing process in the presence of Poraver leads to improved strength properties of the moulding sand (���� �� ). The addition of Poraver's silica to moulding sand did not alter the permeability of the moulding sand samples, and consequently reduced their friability. Microstructure investigations (SEM) of microwave-cured samples have confirmed that heterogeneous sand grains are bonded to one another through a binder film (bridges).
In the paper, presented is a research on effectiveness of absorbing electromagnetic waves at frequency 2.45 GHz by unhardened moulding sands prepared of three kinds of high-silica base and a selected grade of sodium silicate. Measurements of power loss of microwave radiation (Pin) expressed by a total of absorbed power (Pabs), output power (Pout) and reflected power (Pref) were carried-out on a stand of semiautomatic microwave slot line. Values of microwave power loss in the rectangular waveguide filled with unhardened moulding sands served for determining effectiveness of microwave heating. Balance of microwave power loss is of technological and economical importance for manufacture of high-quality casting moulds and cores of various shapes and sizes. It was found that relative density influences parameters of power output and power reflected from samples of moulding sand placed in a waveguide. Absorption expressed by the parameter Pabs is not related to granularity of high-silica base: fine, medium and coarse. It was found that the semiautomatic microwave slot line supports evaluation of effectiveness of microwave absorption on the grounds of power loss measurements and enables statistic description of influence of relative density of the sandmix on penetration of electromagnetic waves in unhardened moulding sands.
Moulding sands containing sodium silicate (water-glass) belong to the group of porous mixture with low resistance to increased humidity. Thanks to hydrophilic properties of hardened or even overheated binder, possible is application of effective methods of hydrous reclamation consisting in its secondary hydration. For the same reason (hydrophilia of the binder), moulds and foundry cores made of high-silica moulding sands with sodium silicate are susceptible to the action of components of atmospheric air, including the contained steam. This paper presents results of a research on the effect of (relative) humidity on mechanical and technological properties of microwave-hardened moulding mixtures. Specimens of the moulding sand containing 1.5 wt% of sodium water-glass with module 2.5 were subjected, in a laboratory climatic chamber, to long-term action of steam contained in the chamber atmosphere. Concentration of water in atmospheric air was stabilized for 28 days (672 h) according to the relative humidity parameter that was ca. 40%, 60% and 80% at constant temperature 20 °C. In three cycles of the examinations, the specimens were taken out from the chamber every 7 days (168 h) and their mechanical and technological parameters were determined. It was found on the grounds of laboratory measurements that moulds and cores hardened with microwaves are susceptible to action of atmospheric air and presence of water (as steam) intensifies action of the air components on glassy film of sodium silicate. Microwave-hardened moulding sands containing sodium silicate may be stored on a longterm basis in strictly determined atmospheric conditions only, at reduced humidity. In spite of a negative effect of steam contained in the air, the examined moulding mixtures maintain a part of their mechanical and technological properties, so the moulds and foundry cores stored in specified, controlled conditions could be still used in manufacture.
Macroporous silica fibers having spherical cavities were fabricated by electrospinning using the spinning solution prepared from the mixed dispersion of tetraethylorthosilicate (TEOS) and polystyrene nanospheres as precursor and sacrificial templates, respectively, by injection through metallic nozzle. By applying electric field, the electro-spun fibers obtained by evaporation-driven self-assembly were collected on flat substrate or rotating drum, followed by the removal of the templates by calcination. The sound absorption coefficient of the porous fibers was measured by impedance tube, and the measured value was larger than 0.9 at high frequency region of incident waves. The surface of the resulting fibers was modified using fluorine-containing silane coupling agent to produce superhydrophobic fibrous materials to prevent the infiltration of humidity.
This paper is devoted to application of adsorption process for cooling power generation in a cooling devices. Construction and working principle of a water-silica gel adsorption chiller has been presented and the basic refrigeration cycle has been discussed. The article outlines behavior of a single-stage adsorption system influenced by changes in cycle time. The effect of cycle time and inlet chilled water temperatures on the main system performance parameters has been analysed
The paper presents the result of investigations of aluminosilicate (low silica - 25 mol%) and phosphate optical fibres. The methods of glass preparation and their properties are showed. A set of physical measurements including: DTA, DSC, DL analysis, absorption spectroscopy, visible and infrared absorption edges and thermo-physical properties were determined. The stable glass compositions were doped with rare earth elements. Selected properties of obtained glasses are: high transmission, refractive index 1.53-1.68, high solubility of RE ions (up to 10 wt%). Double-crucible and rod-in-tube drawing techniques were applied to obtain aluminosilicate and phosphate double clad optical fibres doped with neodymium and ytterbium ions. Luminescence spectra of manufactured glasses and fibres are presented.
Nano technology is an emerging field of interest for civil engineering application. Among the nano materials presently used in concrete, nano-silica possess more pozzolanic nature. It has the capability to react with the free lime during the cement hydration and forms additional C-S-H gel giving strength, impermeability and durability to concrete. Present paper investigates the effects of addition of nano silica in normal strength concrete. Three types of nano-silica in the form of nano suspension having different amount of silica content have been investigated. Mix design has been carried out by using particle packing method. X-Ray diffraction (XRD) analysis has been carried out to find the chemical composition of control concrete and nano modified concrete. Further, experimental investigations have been carried out to characterize the mechanical behaviour in compression, tension and flexure. It has been observed that the addition of nano-silica in normal strength concrete increased the compressive strength and decreased the spilt tensile strength and flexural strength. Also, Rapid chloride permeability test (RCPT) has been conducted to know the chloride permeability of control concrete, nano modified concrete, and nano coated concrete. It has been observed that the chloride permeability is less for nano coated concrete.
In this research reactive powder concrete (RPC) was prepared using sand from North Sinai. The mechanical properties of locally cast RPC were investigated and evaluated by studying the effects of using different cement and silica fume contents and new steel fi bers’ aspect ratios as reinforce-ment for RPC. Specimens’ preparation, curing regimes and testing procedures to evaluate the com-pressive strength, the modulus of elasticity, the indirect tensile strength and the fl exural strength were discussed. A compressive strength of 154.5 MPa, indirect tensile strength of 11.98 MPa, mod-ulus of elasticity of 45.1 GPa and fl exural strength of 30.26 MPa have been achieved for reinforced RPC contains 800 kg/m³ cement content and silica fume content 30% of cement weight. The test results showed some improvements by increasing cement and silica fume contentsas well as adding steel fi bers on the compressive strength, modulus of elasticity and indirect tensile strength.
The goal of this contribution is summary of physical – chemistry properties of usually used foundry silica and no – silica sands in Czech foundries. With the help of dilatometry analysis theoretical assumptions of influence of grain shape and size on dilatation value of sands were confirmed. Determined was the possibility of dilatometry analysis employment for preparing special (hybrid) sands with lower and/or more linear character of dilatation.
Investigations were carried out to ensure the granulated blast furnace (GBF) slag as an alternative mould material in foundry industry by assessing the cast products structure property correlations. Sodium silicate-CO2 process was adopted for preparing the moulds. Three types of moulds were made with slag, silica sand individually and combination of these two with 10% sodium silicate and 20 seconds CO2 gassing time. A356 alloy castings were performed on these newly developed slag moulds. The cast products were investigated for its metallography and mechanical properties. Results reveal that cast products with good surface finish and without any defects were produced. Faster heat transfers in slag moulds enabled the cast products with fine and refined grain structured; and also, lower Secondary Dendrite Arm Spacing (SDAS) values were observed than sand mould. Slag mould casting shows improved mechanical properties like hardness, compression, tensile and impact strength compared to sand mould castings. Two types of tensile fracture modes, namely cleavage pattern with flat surfaces representing Al−Si eutectic zone and the areas of broken Fe-rich intermetallic compounds which appear as flower-like morphology was observed in sand mould castings. In contrast, GBF slag mould castings exhibit majority in dimple fracture morphology with traces of cleavage fracture. Charpy impact fractured surfaces of sand mould castings shows both transgranular and intergranular fracture modes. Only intergranular fracture mode was noticed in both GBF slag and mixed mould castings.
The current casting production of castings brings increased demands for surface and internal quality of the castings. Important factors, that influence the quality of casted components, are the materials used for the manufacture of moulds and cores. For the preparation and production of moulds and cores, in order to achieve a low level of casting defects, then it used a high quality input materials, including various types of sands, modified binders, additives, etc. However, even the most expensive raw materials are not a guarantee to achieve the quality of production. It is always necessary to choose the appropriate combination of input material together with an appropriate proposal for the way of the production, the metallurgical treatment of cast alloy, etc. The aim of this paper is to establish the basic principles for the selection of the base core mixtures components – sands to eliminate defects from the tension, specifically veining. Various silica sand, which are commonly used in foundries of Middle Europe region, were selected and tested.