Al2Cu phase has been obtained by melting pure metals in the electric arc furnace. It has been found that the intermetallic phase undergoes selective corrosion in the H3PO4 aqueous solutions. Aluminium is dissolved, the surface becomes porous and enriched with copper. The corrosion rate equals to 371 ± 17 g·m–2·day–1 (aerated solution) and 284 ± 9 g·m–2·day–1 (deaerated solution). The surface of Al2Cu phase after selective corrosion was characterised by using electrochemical impedance spectroscopy. It was found that the surface area of the specimens increases with temperature due to higher corrosion rate and is between 2137 and 3896 cm2.
Przejdź do artykułu

Abstrakt

In the paper the results and analysis of corrosion tests were presented for low-alloyed cast steel in as-cast state and after heat treatment operations. Such alloys are applied for heavy loaded parts manufacturing, especially for mining industry. The corrosion test were performed in conditions of high salinity, similar to those occurring during the coal mining. The results have shown, that small changes in chemical composition and the heat treatment influence significantly the corrosion behaviour of studied low-alloyed cast steels.
Przejdź do artykułu

Ta strona wykorzystuje pliki 'cookies'. Więcej informacji