The article presents crystallization process of silicon molybdenum ductile cast iron (SiMo). The alloy with 5% silicon content and with variable amounts of Mo in a range of 0-1% was chosen for the research. The carbon content in the analysed alloys did not exceed 3,1%. The studies of crystallization process were based on thermal – derivative analysis (TDA). Chemical composition of all examined samples was analysed with the use of LECO spectrometer. Additionally, the carbon and the sulphur content was determined basing on carbon and sulphur LECO analyser. For metallographic examination, the scanning electron microscopy (SEM) with EDS analyser was used. Disclosed phases have been also tested with the use of X-ray diffraction. The results allowed the description of crystallization processes of silicon molybdenum ductile cast iron using thermal – derivative analysis (TDA). Conducted studies did not allow for the clear identification of all complex phases containing molybdenum, occurring at the grain boundaries. Therefore, the further stages of the research could include the use of a transmission electron microscope to specify the description of complex compounds present in the alloy.
The article presents results of studies of silicon – molybdenum cast iron (4.42% Si, 2.59% Mo and 2.48% C wt.-%) crystallization process. Metallographic analysis was carried out using SEM-scanning electron microscopy with the EDS system. In order to determine the phase composition, X-ray diffraction studies were performed. Thermo-Calc, a computer simulation program, was used to simulate the crystallization process. . The obtained data allowed to describe the effect of some elements on the crystallization process. The silicon phase of MnSi could not be identified during metallographic studies. Also, computer simulation of the crystallization process did not answer the question at which point the silicon phase of MnSi crystallizes in the tested alloy. Therefore, not all results obtained were linked to the registered crystallization process (TDA process). The EDS analysis revealed an unusual distribution of molybdenum in the microstructure of the sample, where it is clearly visible that the area enriched with this element is also the separation of spheroidal graphite. The possibility of occurrence of Mo-rich micro-areas found in graphite is considered. The case is debatable and difficult to resolve at this stage. Perhaps, at such a high concentration of molybdenum (2.59% Mo) in the alloy, conditions are created for simultaneously crystallization of graphite and molybdenum phases.
Silicon – molybdenum cast iron commonly called SiMo due to its unique properties has becoming more and more interesting engineering material. The history and development of this alloy is relatively long but, due to the significant difficulties during the manufacturing process resulting in the lower final quality than expected, it has not been applied to often in practice. The biggest challenge is its brittleness as a result of the carbides precipitations. During last few years, thanks to the many important researches made and the general foundry technology development, the interest in SiMo iron has been rapidly growing, especially for the castings for heavy duty applications like corrosion, high temperature and wear abrasion resistant parts. In the article the heat treatment attempts to improve the microstructure of SiMo castings has been presented. The goal was to destroy or at least to refine and uniformly distribute the carbides precipitations to improve mechanical properties of the exhaust manifold castings for the cars. The experiments were carried out for the alloy contains approx. 4% Si, 1% Mo and 3.2%C. The range of the research included: hardness measuring, standard mechanical properties and microstructure for as-cast state and after that the subsequent heat treatment process with another properties check. The result of the heat treatment was the elimination of pearlite from the metal matrix. Moreover, the changes of the carbide molybdenum – rich phase morphology were observed. The dispersion of the carbides precipitations in the carbides area was observed. The experiments proved the possibility to control the microstructure and the mechanical properties of the SiMo castings by means of heat treatment but only to some extent.
The article presents results of pitting corrosion studies of selected silicon cast irons. The range of studies included low, medium and high silicon cast iron. The amount of alloying addition (Si) in examined cast irons was between 5 to 25 %. Experimental melts of silicon cast irons [1-3] were conducted in Department of Foundry of Silesian University of Technology in Gliwice and pitting corrosion resistance tests were performed in Faculty of Biomedical Engineering in Department of Biomaterials and Medical Devices Engineering of Silesian University of Technology in Zabrze. In tests of corrosion resistance the potentiostat VoltaLab PGP201 was used. Results obtained in those research complement the knowledge about the corrosion resistance of iron alloys with carbon containing Si alloying addition above 17 % [4-6]. Obtained results were supplemented with metallographic examinations using scanning electron microscopy. The analysis of chemical composition for cast irons using Leco spectrometer was done and the content of alloying element (silicon) was also determined using the gravimetric method in the laboratory of the Institute of Welding in Gliwice. The compounds of microstructure were identify by X-ray diffraction.
The paper presents the research results of horizontal continuous casting of ingots of aluminium alloy containing 2% wt. silicon (AlSi2). Together with the casting velocity (velocity of ingot movement) we considered the influence of electromagnetic stirring in the area of the continuous casting mould on refinement of the ingot’s primary structure and their selected mechanical properties, i.e. tensile strength, yield strength, hardness and elongation. The effect of primary structure refinement and mechanical properties obtained by electromagnetic stirring was compared with refinement obtained by using traditional inoculation, which consists in introducing additives, i.e. Ti, B and Sr, to the metal bath. On the basis of the obtained results we confirmed that inoculation done by electromagnetic stirring in the range of the continuous casting mould guarantees improved mechanical properties and also decreases the negative influence of casting velocity, thus increasing the structure of AlSi2 continuous ingots.
In paper is presented idea of construction and influence of selected parts of stand of horizontal continuous casting on quality of pure Al and AlSi2 alloy ingots. The main parts of the made stand belong to induction furnace, which is also tundish, water cooled continuous casting mould, system of recooling, system of continuous ingot drawing and cutting. Mainly was considered influence of electromagnetic stirrer, which was placed in continuous casting mould on refinement of ingots structure. Effect of structure refinement obtained by influence of electromagnetic stirring was compared with refinement obtained by use of traditional inoculation, which consists in introducing of additives i.e. Ti and B to metal bath. The results of studies show possibility of effective refinement of Al and AlSi2 alloy primary structure, only with use of horizontal electromagnetic field and without necessity of application of inoculants. This method of inoculation is important, because inoculants decrease the degree of purity and electrical conductivity of pure aluminum and moreover are reason of point cracks formation during rolling of ingots.
In paper is presented results of studies concerning ingot of Al with a purity of 99.5% cast with use of stand of horizontal continuous casting. Mainly together with casting velocity was considered influence of electromagnetic stirrer, which was placed in continuous casting mould on refinement of ingots structure and theirs usability to plastic deformation. Effect of structure refinement and usability to plastic deformation obtained by influence of electromagnetic stirring was compared with refinement obtained by use of traditional inoculation, which consists in introducing of additives i.e. Ti and B to metal bath. On the basis of obtained results was affirmed that inoculation realized by electromagnetic stirring in range of continuous casting mould guarantees improvement in structure refinement and usability to rolling of pure Al continuous ingots.