The phytotoxic effects of fluoride and its derivatives on the seeds and seedlings of the Colobanthus apetalus and Colobanthus quitensis were studied. This is a first study to evaluate the influence of sodium fluoride (NaF) on the morphophysiological and biochemical processes on two Colobanthus species. The influence of various concentrations of NaF (9 mM, 19 mM, 29 mM) on the germination capacity and germination rate of seeds, seedlings growth and the proline content of plant tissues was analyzed under laboratory conditions (20/10°C, 12/12 h). The seeds of C. apetalus were collected from a greenhouse, whereas the seeds of C. quitensis were collected in Antarctica and in a greenhouse (Olsztyn, Poland). The tested concentrations of NaF did not suppress the germination of C. apetalus seeds, but the germination of C. quitensis seeds was inhibited. Sodium fluoride mainly inhibited root growth of C. apetalus and C. quitensis. In both analyzed species, the free proline content of seedlings increased significantly under exposure to NaF. The results of this study clearly indicate that C. apetalus and C. quitensis are highly resistant to NaF stress.
The paper presents an innovative method of creating the layered castings. The innovation relies on application the 3D printing insert obtaining in SLM (selective laser melting) method. This type of scaffold insert made from pure Ti powder, was placed into mould cavity directly before pouring by grey cast iron. In result of used method was obtained grey cast iron casting with surface layer reinforced by titanium carbides. In range of studies were carried out metallographic researches using light microscope and scanning electron microscope, microhardness measurements and abrasive wear resistance. On the basis of obtaining results was stated that there is a possibility of reinforcing surface layer of the grey cast iron casting by using 3D printing scaffold insert in the method of mould cavity preparation. Moreover there was a local increase in hardness and abrasive wear resistance in spite of the precipitation of titanium carbides in surface layer of grey cast iron. While the usable properties of composite surface layer obtained in result of use of the method presented in the paper, strongly depend of dimensions of scaffold insert, mainly parameters Re and Ri.
The paper presents selected granular ceramic materials available on the Polish market. Their characteristics have been determined in the aspect on application in the production of iron alloy-ceramic composite. The possibility of obtaining a composite layer by means of bulk grains in molds of plates were considered, which was the foundation for experimental molds to be used in service tests. On the basis of obtaining results was stated that the knowledge of the characteristics of bulk grains enables the calculation of their quantity necessary for the composite production. When using the bulk grains the thickness of the composite layer is restricted by the thermal relations (cooler) and the physical phenomena (buoyancy, metal static pressure). Increasing amount of grains above definite condition causes surface defects in the castings. Each casting, due to its weight, shape and place of composite layer production requires an individual approach, both at the stage of formation and that of calculation of the required quantity of ceramic grains.
This paper presents matters related to production of ceramic and cast iron composite. The composite was made with the use of a foam structured ceramic insert. The tests included measuring of hardness, impact strength and resistance to abrasive wear of the composite produced. On the basis of obtaining results was stated that the use of foamed ceramic filters provides good conditions of filling a ceramic framework with molten grey or chromium cast iron. The growth of hardness of the ceramic- grey cast iron composite is ca. 60% as compared to the grey cast iron hardness. The growth of hardness of the ceramic- chromium cast iron composite is slight and does not exceed 5 % in comparison to the chromium cast iron. Introduction of the ceramic inserts deteriorates the cast iron impact strength by ca. 20 - 30 %. The use of ceramic inserts increases the resistance to abrasive wear in case of grey cast iron by ca. 13% and in case of the chromium cast iron by ca. 10 %.
The paper presents a method of producing a grey cast iron casting locally reinforced with a titanium insert printed using SLM method (Selective Laser Melting). This article attempts to examine the impact of the selected geometry of titanium spatial insert on the surface layer formation on grey cast iron. The scope of the research focuses on metallographic examination - observation and analysis of the structure of the reinforced surface layer on a light and scanning microscope and a hardness measurement of the titanium layer area. Based on the obtained results, it was concluded that the reaction between titanium insert and metal (grey cast iron) locally develops numerous carbides precipitation (mainly TiC particles), which increases the hardness of the reinforced surface layer and local strengthening of the material. The ratio between the thickness of the support part (grey cast iron) and the working part (titanium insert) affects the resulting layers connection structure. The properties of the obtained reinforced surface layer depend mainly on the geometry of the insert (primarily on the internal dimensions of the connector) and the volume of the casting affecting the re-melting of the insert. A more concentrated structure of carbides precipitation occurs in castings with a full connector insert.