For the purpose of making of a solid body of an electric guitar the acoustic- and mechanical properties of walnut- (Juglans regia L.) and ash wood (Fraxinus excelsior L.) were researched. The acoustic properties were determined in a flexural vibration response of laboratory conditioned wood elements of 430 × 186 × 42.8 mm used for making of a solid body of an electric guitar. The velocity of shearand compression ultrasonic waves was additionally determined in parallel small oriented samples of 80 × 40 × 40 mm. The research confirmed better mechanical properties of ash wood, that is, the larger modulus of elasticity and shear modules in all anatomical directions and planes. The acoustic quality of ash wood was better only in the basic vibration mode. Walnut was, on the other hand, lighter and more homogenous and had lower acoustic- and mechanical anisotropy. Additionally, reduced damping of walnut at higher vibration modes is assumed to have a positive impact on the vibration response of future modelled and built solid bodies of electric guitars. When choosing walnut wood, better energy transfer is expected at a similar string playing frequency and a structure resonance of the electric guitar.
Foundry dust from blasting and grinding of castings contain a high amount of iron, ergo it is possible its recycling in foundry process. Dust was compacted by briquetting, two kinds of briquettes were prepared (A contained 95% magnetic part of dust from casting blasting +5% bentonite and B contained 95% mixture of dust from casting grinding and magnetic part of dust from casting blasting + 5% bentonite) and used as a part of charge into the electric induction furnace. It was found that addition of briquettes has had an influence of a chemical composition of cast iron above all on content of sulphur, phosphorus and silicon. It was not reflected in decrease in tensile strength and in microstructure. Yield of metal from briquettes was not lower then 70%.
The discovery of (BaxCa1-x)(ZryTi1-x)O3 lead-free ceramics drawn a lot of attention to those novel materials because of their excellent piezoelectric properties. However, quite a little attention has been paid to other features of the material. This article reports a wide range of research, including composition, structure and microstructure, dielectric response and impedance spectroscopy in order to systematize and expand knowledge about this peculiar ceramics and strontium doping effect on its properties. In order to test that influence a series of samples with various strontium concentration, precisely the admixtures of 0.02, 0.04 and 0.06 mol% were prepared, as well as basic ceramics to compare obtained results.