This study presents results of stress rupture test of MAR-M-509 cobalt alloy samples, as-cast and after surface refining with a concentrated stream of heat. Tests were conducted on samples of MAR-M-509 alloy castings, obtained using the lost-wax method. Casting structure refining was performed with the GTAW method in argon atmosphere, using the current I = 200 A and electrical arc scanning velocity vs = 100, 150, 200 and 250 mm/min. The effect of rapid resolidification of the MAR-M-509 alloy on the microstructure was examined and significant improvement in stress rupture test was observed.
The paper summarises results of measurements of remelting area geometry, thermal efficiency and melting efficiency characterising the surface remelting process applied to castings of MAR-M-509 cobalt alloy. The remelting process was carried out with the use of GTAW (Gas Tungsten Arc Welding) method in protective atmosphere of helium, at the electric current intensity in the range from 100 A to 300 A, and the electric arc scanning velocity vs in the range from 200 mm/min to 800 mm/min. The effect of current intensity and electric arc scanning velocity on geometrical parameters of remeltings, thermal efficiency, and melting efficiency characterising the remelting process has been determined.