The paper proposes a methodology useful in verification of results of dilatometric tests aimed at determination of temperatures defining the start and the end of eutectoid transformation in the course of ductile cast iron cooling, based on quenching techniques and metallographic examination. For an industrial melt of ductile cast iron, the effect of the rate of cooling after austenitization at temperature 900°C carried out for 30 minutes on temperatures TAr1 start and TAr1 end was determined. The heating rates applied in the study were the same as the cooling rates and equaled 30, 60, 90, 150, and 300°C/h. It has been found that with increasing cooling rate, values of temperatures TAr1 start and TAr1 end decrease by several dozen degrees.
The results of studies on the use of magnesium alloy in modern Tundish for production of vermicular graphite cast irons were described. This paper describes the results of using a low-magnesium ferrosilicon alloy for the production of vermicular graphite cast irons. The paper presents a vermicular (and nodular) graphite in different walled castings. The results of trials have shown that the magnesium Tundish process can produce high quality vermicular graphite irons under the specific industrial conditions of Foundries - Odlewnie Polskie S.A. in Starachowice. In this work describes too preliminary studies on the oxygen state in cast iron and their effect on graphite crystallization.
This article deals with the technology and principles of the laser cutting of ductile cast iron. The properties of the CO2laser beam, input parameters of the laser cutting, assist gases, the interaction of cut material and the stability of cutting process are described. The commonly used material (nodular cast iron - share of about 25% of all castings on the market) and the method of the laser cutting of that material, including the technological parameters that influence the cutting edge, are characterized. Next, the application and use of this method in mechanical engineering practice is described, focusing on fixing and renovation of mechanical components such as removing the inflow gate from castings with the desired quality of the cut, without the further using of the chip machining technology. Experimental samples from the nodular cast iron were created by using different technological parameters of laser cutting. The heat affected zone (HAZ), its width, microstructure and roughness parameter Pt was monitored on the experimental samples (of thickness t = 13 mm). The technological parameters that were varied during the experiments included the type of assist gases (N2and O2), to be more specific the ratio of gases, and the cutting speed, which ranged from 1.6 m/min to 0.32 m/min. Both parameters were changed until the desired properties were achieved.
The paper attempts to analyze distortions of cast iron and cast steel rings, after heat treatment cycles. The factors influencing distortion are: chemical composition of material, sample geometry, manufacturing process, hardenability, temperature and heat treatment method. Standard distortion tests are performed on C-ring samples. We selected a ring-model, which approximate the actual part, so that findings apply to gear rings. Because distortion depends on so many variables, this study followed strictly defined procedures. The research was started by specifying the appropriate geometry of the samples. Then, the heat treatment was conducted and samples were measured again. The obtained results allow to determine the value of the resulting distortion and their admissibility. The research will be used to evaluate the possibility of using the material to produce parts of equipment operated under extreme load conditions.
The article describes the detection of a defect in a cast iron casting. It analyzes the cause of the crack in the Turbine Component casting. In this article, we are focusing on a particular turbine casting that is commonly used in automobiles as one of the components for turbochargers. The turbine is a casting made of ductile cast iron with a visible crack on the naked eye. The formation of cracks in castings is a common but undesirable phenomenon in the foundry practice. It is important to identify the errors, but also to know the cause of defects in castings. The solution is a detailed error analysis. In this paper I used metallographic analysis and magnetic powder method. The crack formation is due to tension in the casting, which results in tensile, shear, or shear forces. The crack formation kinetics is difficult because it is still very low during hardening and shortly after the casting is overloaded. The crack is most often due to core resistance or shrinkage molds that begin after the surface layer is tightened when the strength of the material is negligible to the end of the crystallisation.
The paper deals with the issue of potential for improvement of resistance of wood chip fine grinders to abrasive wear by providing them with WCCoCr coating applied with the use of atmospheric plasma spraying (APS). The study focused on establishing parameters of the technological process of spraying a 250–270 μm thick coating onto surface of ductile cast iron castings used to date as grinder linings. The presented data include results of microstructure examination, chemical composition analysis, HV hardness measurements, and scratch tests for both previous and new variant of linings. The obtained scratch test results indicate that the material of the coating is characterized with definitely lower susceptibility to scratching. The scratch made on coating was 75–84 μm wide and 7.2–8.2 μm deep, while the scratch on cast iron was distinctly wider (200–220 μm) and deeper (8.5–12.8 μm). In case of cast iron, the range of variability in scratch width and depth was definitely larger. This can be explained with large difference in hardness of individual components of microstructure of cast iron and significantly larger plastic deformation of cast iron compared to the coating revealed in the course of indenter motion over surfaces of the two materials. It has been found that application of WCCoCr coating offered better resistance of lining surfaces to scratching which can be considered a rationale for undertaking in-service tests.
The objective of the research was to determine the influence of boron on the crystallization process and microstructure of ductile cast iron. In the case of ductile cast iron it is a vital issue because even as little as trace presence of boron changes the properties of ductile cast iron in a significant way. With the use of a new ATD-4 (TDA) tester and CRYSTALDIGRPAH converter it was possible to measure the crystallization process parameters of the same alloy with four different contents of boron in one mould. Four samples with different boron contents were extracted, their microhardness was measured and quantitative analysis of microstructure was conducted. Obtained results allowed to state that with increasing content of boron the amount of graphite precipitates decreases, the amount of pearlite precipitates increases, the shape of graphite precipitates deteriorates and hardness increases. It is also planned to perform additional testings with boron contents between previously tested values.
The paper presents the results of experimental-simulation tests of expansion-shrinkage phenomena occurring in cast iron castings. The tests were based on the standard test for inspecting the tendency of steel-carbon alloys to create compacted discontinuities of the pipe shrinkage type. The cast alloy was a high-silicone ductile iron of GJS - 600 - 10 grade. The validation regarding correctness of prognoses of the shrinkage defects was applied mostly to the simulation code (system) NovaFlow & Solid CV (NFS CV). The obtained results were referred to the results obtained using the Procast system (macro- and micromodel). The analysis of sensitivity of the modules responsible for predicting the shrinkage discontinuities on selected pre-processing parameters was performed, focusing mostly on critical fractions concerning the feeding flows (mass and capillary) and variation of initial temperature of the alloy in the mould and heat transfer coefficient (HTC) on the casting - chill interface.
The goal of this article is non-destructive ultrasonic testing of internal castings defects. Our task was to cast several samples with defects like porosity and cavities (where belongs mostly shrinkages) and then pass these samples under ultrasonic testing. The characteristics of ultrasonic control of castings are presented in the theoretical part of this article. Ultrasonic control is a volume non-destructive method that can detect internal defects in controlled materials without damaging the construction. It is one of the most widely used methods of volume non-destructive testing. For experimental control were made several cylindrical samples from ferritic grey and ductile cast iron. Because of the form and dispersion of graphite of grey cast iron it was not possible to make ultrasonic records on this casting with probe we used, so we worked only with ductile cast iron. Ultrasonic records of casting control are shown and described in the experimental part. The evaluation of the measurement results and the reliability of the ultrasonic method in castings control is listed at the end of this article.
In the family of iron-based alloys, ductile iron enjoys the highest rate of development, finding application in various industries. Ductile iron or the cast iron with spheroidal graphite can be manufactured by various methods. One of them is the Inmold spheroidization process characterized by different technological solutions, developed mainly to increase the process efficiency. So far, however, none of the solutions has been based on the use of a reactor made outside the casting mould cavity. The method of spheroidization inside the casting mould using a reaction chamber developed at the Foundry Research Institute is an innovative way of cast iron treatment. The innovative character of this method consists in the use of properly designed and manufactured reactor placed in the casting mould cavity. Owing to this solution, the Inmold process can be carried out in moulds with both horizontal and vertical parting plane. The study presents the results of examinations of the microstructure of graphite precipitates and metal matrix of castings after spheroidization carried out by the Inmold process using a reactor and mould with vertical parting plane. Special pattern assembly was made for the tests to reproduce plates with wall thicknesses of 3; 5; 7; 10; 20 and 30 mm. The content of residual magnesium was determined for all tested castings, while for castings of plates with a wall thickness equal to or larger than 10 mm, testing of mechanical properties was additionally performed.
Production of spheroidal graphite cast iron is today quite mastered technology. There are many methods achieving the nodular graphite morphology. Each of these methods have specific characteristics and requirements to technical support, properties and the type of applied modifier. Selection of the spheroidization method is dependent on foundry disposition, production character, economic balance, quality requirements, etc. In case of centrifugally casting the core, which fills body and neck of the roll, is created by ductile iron. Considering the sophisticated production of centrifugally cast rolls for hot rolling mills it is necessary to ensure a high reproducibility and reliability of ductile cast iron production quality in the bulk range of 9-18 t per tapping. These conditions are in the Roll Foundry in Vítkovicke Slevarny, spol. s r.o. provided and verified mastered overpour method and the newly injection of cored wire in the melt.
An intentional change in material properties is an important condition for castings production. It is one way how to meet the casting requirements of how to adapt the material properties to the operating conditions. Centrifugally cast rolls are multi-layer rollers, castings. The working layer of the barrel is called the "shell" and the body of the roll and the necks rolls are called "core". The article deals with the influence of the properties of the core iron. Earlier laboratory experiments were primary analysed for metallographic analysis and mechanical properties. These data were compared back to the experiments. The results of these laboratory working were later applied in the operating conditions of the roll foundry Vítkovitcké slévárny, spol. s r.o. The spun cast roll produced with the applied metallurgical processing change was supplied to the hot strip mill. There were monitored the positive effect of the change of the metallurgical process of the production of the core iron on the useful properties of the centrifugally cast roll. The experiment was done in order to increase the mechanical properties of ductile pearlite ductile iron. The copper in these core iron material increases the hardness and strength primarily.