Iron is presented as an impurity in Al-Si alloys and occurs in the form of the β-Al5FeSi phase formations. The presence of iron and other elements in the alloy causes the formation of large intermetallic phases. Due to the high brittleness of this phase, it reduces the mechanical properties and increases the porosity. Manganese is used to inhibit the formation of this detrimental phase. It changes the morphology of the phase to polyhedral crystals, skeletal formations, or Chinese script. The present article deals with the influence of various amounts of manganese (0.1; 0.2; 0.4; 0.6 wt. %) on the formation of iron-based intermetallic phases in the AlSi7Mg0.3 alloy with different levels of iron content (0.4; 0.8, 1.2 wt. %). The increase of iron content in each alloy caused the creation of more intermetallic compounds and this effect has been more significant with higher concentrations of manganese. In alloys where the amount of 1.2 wt. % iron is present, the shape of eutectic silicon grain changes from angular to short needle type.
Manganese is an effective element used for the modification of needle intermetallic phases in Al-Si alloy. These particles seriously degrade mechanical characteristics of the alloy and promote the formation of porosity. By adding manganese the particles are being excluded in more compact shape of “Chinese script” or skeletal form, which are less initiative to cracks as Al5FeSi phase. In the present article, AlSi7Mg0.3 aluminium foundry alloy with several manganese content were studied. The alloy was controlled pollution for achieve higher iron content (about 0.7 wt. % Fe). The manganese were added in amount of 0.2 wt. %, 0.6 wt. %, 1.0 wt. % and 1.4 wt. %. The influence of the alloying element on the process of crystallization of intermetallic phases were compared to microstructural observations. The results indicate that increasing manganese content (> 0.2 wt. % Mn) lead to increase the temperature of solidification iron rich phase (TAl5FeSi) and reduction this particles. The temperature of nucleation Al-Si eutectic increase with higher manganese content also. At adding 1.4 wt. % Mn grain refinement and skeleton particles were observed.
In Al-Si alloy the iron is the most common impurity and with presence of other elements in alloy creates the intermetallic compounds, which decreases mechanical properties and increases of porosity. The cause of the negative effect of intermetallic particles on the mechanical properties is that it is more easily break off the tension load as the aluminium matrix or small particles of silicon. By adding suitable alloying elements, also known as iron correctors, is possible to reduce this harmful effect. In the article is evaluated influence of manganese on microstructure with performed EDX analysis selected intermetallic phases and tensile test and measurement of length of Al5FeSi phase. For realization experiments was used AlSi7Mg0.3 alloy with increased iron content. Manganese was added in the amount 0.3 wt. %, 0.6 wt. %, 0.8 wt.% and 1,2 wt. %. From performed measurements it has been concluded, that increased amount of manganese, i.e. Mn/Fe ratio, does not have significant influence on mechanical properties AlSi7Mg0.3 alloy in the melted state.
The paper deals with the influence of manganese in AlSi7Mg0.3 alloy with higher iron content. Main aim is to eliminate harmful effect of intermetallic – iron based phases. Manganese in an alloy having an iron content of about 0.7 wt. % was graded at levels from 0.3 to 1.4 wt. %. In the paper, the effect of manganese is evaluated with respect to the resulting mechanical properties, also after the heat treatment (T6). Morphology of the excluded intermetallic phases and the character of the crystallisation of the alloy was also evaluated. From the obtained results it can be concluded that the increasing level of manganese in the alloy leads to an increase in the temperature of the β-Al5FeSi phase formation and therefore its elimination. Reducing the amount of β-Al5FeSi phase in the structure results in an improvement of the mechanical properties (observed at levels of 0.3 to 0.8 wt. % Mn). The highest addition of Mn (1.4 wt.%) leads to a decrease in the temperature corresponding to the formation of eutectic silicon, which has a positive influence on the structure, but at the same time the negative sludge particles were also present