This article focuses on the study of the influence of remelting and subsequent natural and artificial ageing on the structure of recycled AlSi9Cu3 alloy with increased iron content. The assessed changes in eutectic silicon and iron-based intermetallic phases were carried out using optical and scanning electron microscopy. The degradation of the eutectic silicon morphology due to remelting occurred only at the highest numbers of remelting. The effect of remelting the investigated alloy, which is accompanied by a gradual increase in wt. % Fe, began to manifest significantly through a change in the length of the ferric phases after the fourth remelting. As expected, the artificial ageing process has proven to be more effective than natural ageing. It has led to a change in the eutectic silicon morphology and has been beneficial in reducing the lengths of adverse ferric phases. The use of alloys with higher numbers of remelting, or with greater “contamination”, for the manufacture of shape-challenging castings is possible when using a suitable method of eliminating the negative factors of the remelting process. The results of our investigation show a suitable method of the above elimination the application of heat treatment T5 – via artificial ageing.
Secondary or multiple remelted alloys are common materials used in foundries. For secondary (recycled) Al-Si-Cu alloys, the major problem is the increased iron presence. Iron is the most common impurity and with presence of other elements in alloy creates the intermetallic compounds, which may negatively affect the structure. The paper deals with effect of multiple remelting on the microstructure of the AlS9iCu3 alloy with increased iron content to about 1.4 wt. %. The evaluation of the microstructure is focused on the morphology of iron-base intermetallic phases in caste state, after the heat treatment (T5) and after natural aging. The occurrence of the sludge phases was also observed. From the obtained results can be concluded that the multiple remelting leads to change of chemical composition, changes in the final microstructure and also increases sludge phases formation. The use of heat treatment T5 led to a positive change of microstructure, while the effect of natural aging is beneficial only to the 3rd remelting.
The paper deals with influence of multiple remelting on AlSi9Cu3 alloy with higher iron content on chosen mechanical properties. Multiple remelting may in various ways influence mechanical, foundry properties, gas saturation, shrinkage cavity, fluidity etc. of alloy. Higher presence of iron in Al-Si cast alloys is common problem mainly in secondary (recycled) aluminium alloys. In Al-Si alloy the iron is the most common impurity and with presence of other elements in alloy creates the intermetallic compounds, which decreases mechanical properties. Iron in the used alloy was increased to about 1.4 wt. %, so that the influence of increased iron content can be investigated. In the paper, the effect of multiple remelting is evaluated with respect to the resulting mechanical properties in cast state, after the heat treatment (T5) and after natural aging. From the obtained results it can be concluded that the multiple remelting leads to change of chemical composition and affect the mechanical properties.