The paper presents research results of multilayer systems composed of alternate Cu/Ni layers. The layers thickness obtained by the galvanic treatment was determined by using the transmission electron microscopy and X-ray diffraction method in the grazing incidence diffraction geometry. The surface morphology was observed using scanning electron microscope with EDS microanalysis. Observation of the surface topography of systems using the atomic force microscope was also carried out.
The aim of the paper is to study the effect of zinc addition on the corrosion behavior of Ca65–xMg17.5Zn17.5+x (x = 0, 2.5, 5 at.%) alloys in simulated physiological fluids at 37°C. The electrochemical measurements allowed to determine a corrosion potential, which showed a positive shift from –1.60 V for Ca65Mg17.5Zn17.5 alloy to –1.58 V for Ca60Mg17.5Zn22.5 alloy, adequately. The more significant decrease of hydrogen evolution was noticed for Ca60Mg17.5Zn22.5 alloy (22.4 ml/cm2) than for Ca62.5Mg17.5Zn20 and Ca65Mg17.5Zn17.5 samples (29.9 ml/cm2 and 46.4 ml/cm2), consequently. The corrosion products after immersion tests in Ringer’s solution during 1 h were identified by X-ray diffraction and X-ray photoelectron spectroscopy as calcium, magnesium oxides, carbonates, hydroxides and calcium hydrate.